Engineering-Like 3D resin, Black, 1L
SKU
EL-3D-Black-1L
Not available
52.71EUR 42.00EUR
- Buy 2 for 50.20EUR 40.00EUR each and save 5%
Engineering-Like 3D printing resin, Black, 1L, 405nm UV Cure
NEW version of ABS like resin-- Engineering Like Resin
Better mechanical property and low water absorption.
Great tenacity, it is not brittle.
ABS property
Anti-scratch
Super strong with tenacity
Great weathering
Suitable for different post processing like drilling, screwing etc.
Clean with IPA
| Technical specification | |
| Flexural modulus | 1.19 - 2.53 Mpa |
| Impact strenght |
60-80 (J/m) |
| Hot deformation temp | 65-80C |
| Linear shrinkage | 1.05-1.35% |
| Tensile strenght | 42-62 Mpa |
| Tensile modulus | 1.86-2.64 Mpa |
| Elongation at break | 4-10% |
| Hardness (Shore D) | 80-85C |
| Viscosity | 150-350MPa-s |
| Printing parameter | |
| Printing time | For LCD printer, bottom layer 30-70s and each layer exposure time 4-12s, for example, layer thickness 50 micron on Anycubic printer, base 50s while each layer 8s. For DLP printer, bottom 5-15s and each layer 1-5s. |
| Cleaning and post-curing | Cleaning with flush water and brush it gently with a soft brush, and then drying it with cold air. |
| Post-curing | 1. The curing time is proportional to the volume of the work piece and inversely proportional to the optical power of the curing chamber. Example: 100 watt LED curing box, jewelry jobs is recommended to be cured with soaking in water for 20-30 minutes. 2. The post-cure time of dental casting resin, dental non-casting resin and jewelry mold resin shall not more than 5 minutes. 3. Work-pieces should be in the water during post-curing to prevent deformation especially for dental and jewelry. 4. Don’t forget to use cool air to dry it after post-curing. |